History of zinc–antimony alloys and zinc antimonide
The first reported use of zinc-antimony alloys was in the original work of T. J. Seebeck on thermoelectricity,[3] a scientist who would then give his name to the Seebeck effect. By the 1860s, Moses G. Farmer, an American inventor, had developed the first high powered thermoelectric generator based on using a zinc-antimony alloy with a composition very close to stoichiometric ZnSb. He showed this generator at the 1867 Paris Exposition where it was carefully studied and copied (with minor modifications) by a number of people including Clamond.[clarification needed] Farmer finally received the patent on his generator in 1870. George H. Cove patented a thermoelectric generator based on a Zn-Sb alloy in the early 1900s. His patent [4] claimed that the voltage and current for six "joints" was 3V at 3A. This was a far higher output than would be expected from a thermoelectric couple, and was possibly the first demonstration of the thermophotovoltaic effect, as the bandgap for ZnSb is 0.56eV, which under ideal conditions[according to whom?] could yield close to 0.5V per diode.[citation needed] The next researcher to work with the material was Mária Telkes while she was at Westinghouse in Pittsburgh during the 1930s. Interest was revived again with the discovery of the higher bandgap Zn4Sb3 material in the 1990s.
References
^
Lide, David R. (1998), Handbook of Chemistry and Physics (87 ed.), Boca Raton, Florida: CRC Press, pp. 4–95, ISBN0-8493-0594-2
^Li, Jing-Bo; Record, Marie-Christine; Tedenac, Jean-Claude (2007). "A thermodynamic assessment of the Sb-Zn system". Journal of Alloys and Compounds. 438 (1–2): 171–177. doi:10.1016/j.jallcom.2006.08.035.